HSCHeat Shrinkable crimp splices
防水热缩中接端子
应用
HSC是由聚烯烃和热熔胶复合而生成的热收缩套管,用于保护连接、防水防腐蚀,可以在粗糙的环境中加强固定和防震动,具有很好的绝缘保护电子连接器的功能。与常规的连接器相比,具有耐久性、易于安装、安装成本低的优势。
特性
收缩率3:1
优异的防水性能
材料优异的延伸性能,抗机械损害
透明度佳,提高更好的抗拉力
高弹性能,管材不易变形
操作温度范围
操作温度: -55℃~125℃
开始收缩温度: 80℃
最低完全收缩温度: 130℃
性能参数
Test Item |
Characteristics |
Test condition |
|
Unaged |
Tensile strength |
Min. 18MPa |
Room temp. |
Elongation |
Min. 200% |
||
Aged |
Tensile strength |
Min. 11.5MPa |
150℃/7 days |
Elongation |
Min. 100% |
||
Voltage withstand and breakdown Voltage(Unaged) |
Withstand 2.5 KV for 1minute and breakdown |
Room temp. |
|
Voltage withstand and breakdown Voltage(Aged) |
Withstand 2.5 KV for 1minute and breakdown at least half of unaged breakdown voltage |
150℃/7 days |
|
Copper corrosion |
No corrosion of bare copper |
150℃/7 days |
|
Copper stability |
No sign of degradation Min.Elongation 100% |
150℃/7 days |
|
Cold bend |
No crack |
-40℃/4 hrs |
|
Maximum secant modulus(2%) |
250 MPa |
- |
|
Volume resistivity |
Min.1014Ω-cm |
- |
|
Heat shock |
No crack |
200℃/4 hrs |
产品规格
Part. No |
Wire Range |
Dimension(mm) |
Heat shrink tube(mm) |
Insulator |
Color |
Approval |
|||||
A.W.G |
mm2 |
OD |
B |
L2 |
OD |
A |
L1 |
||||
HSC-0.5 |
26-22 |
0.2-0.5 |
2.1 |
1.3 |
10 |
4.1 |
3.2 |
26.0 |
PE |
Yellow |
RoHS |
HSC-1 |
22-18 |
0.5-1.0 |
3.3 |
1.7 |
15 |
5.9 |
4.7 |
36.0 |
PE |
Red |
RoHS |
HSC-2 |
16-14 |
1.5-2.5 |
4.0 |
2.4 |
15 |
7.1 |
5.7 |
36.0 |
PE |
Blue |
RoHS |
HSC-3 |
12-10 |
4.0-6.0 |
5.5 |
3.5 |
15 |
8.0 |
6.7 |
42.0 |
PE |
Yellow |
RoHS |
HSC-3.5 |
14-12 |
2.5-4 |
5.5 |
4.1 |
20 |
7.8 |
6.5 |
38 |
PE |
Black |
RoHS |
HSC-3.5(薄) |
14-12 |
2.5-4 |
5.4 |
4.3 |
15 |
7.8 |
6.5 |
38 |
PE |
Black |
RoHS |
HSC-8 |
8 |
10 |
7.0 |
5.8 |
21 |
9.5 |
8.0 |
42.0 |
PE |
Yellow |
RoHS |